ISO 6892 Metallic materials — Tensile testing —부분 1:상온에서의 시험 방법
1 Scope
This part of ISO 6892 specifies the method for tensile testing of metallic materials and defines the mechanical
properties which can be determined at room temperature.
참고 부록 A는 컴퓨터 제어 시험기에 대한 보완적인 권장 사항을 나타냅니다..
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, 인용 된 버전 만 적용됩니다.. 날짜가 없는 참조의 경우, the latest edition of the referenced
document (including any amendments) applies.
ISO 377, Steel and steel products — Location and preparation of samples and test pieces for mechanical
testing
ISO 2566-1, Steel — Conversion of elongation values — Part 1: Carbon and low alloy steels
ISO 2566-2, Steel — Conversion of elongation values — Part 2: Austenitic steels
ISO 7500-1, Metallic materials — Verification of static uniaxial testing machines — Part 1:
Tension/compression testing machines — Verification and calibration of the force-measuring system
ISO 9513, Metallic materials — Calibration of extensometers used in uniaxial testing
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1 gauge length L
length of the parallel portion of the test piece on which elongation is measured at any moment during the test
3.1.1 original gauge length Lo
length between gauge length (3.1) marks on the piece measured at room temperature before the test
3.1.2 final gauge length after rupture Lu
length between gauge length (3.1) marks on the test piece measured after rupture, at room temperature, the
two pieces having been carefully fitted back together so that their axes lie in a straight line
NOTE Adapted from ISO/TR 25679:2005[3].
3.2 parallel length Lc
length of the parallel reduced section of the test piece.
3.3 elongation
increase in the original gauge length (3.1.1) at any moment during the test
3.4 percentage elongation
elongation expressed as a percentage of the original gauge length, Lo (3.1.1)
3.4.1 percentage permanent elongation
increase in the original gauge length (3.1.1) of a test piece after removal of a specified stress, expressed as a percentage of the original gauge length, Lo
3.4.2 percentage elongation after fracture A
permanent elongation of the gauge length after fracture, (Lu − Lo), expressed as a percentage of the original
gauge length, Lo 1) 5,65 So=5 (4So/ð) .
3.5 신율계 게이지 길이 Le
initial extensometer gauge length used for measurement of extension by means of an extensometer
확장
increase in the 신율계 게이지 길이, Le (3.5), at any moment during the test
3.6.1 percentage extension
“strain”
extension expressed as a percentage of the 신율계 게이지 길이, Le (3.5)
3.6.2 percentage permanent extension
increase in the extensometer gauge length, after removal of a specified stress from the test piece, expressed
as a percentage of the 신율계 게이지 길이, Le (3.5)
3.6.3 percentage yield point extension
See Figure 7.
3.6.4 percentage total extension at maximum force Agt
total extension (elastic extension plus plastic extension) at maximum force, expressed as a percentage of the
신율계 게이지 길이, Le (3.5)
3.6.5 percentage plastic extension at maximum force Ag
plastic extension at maximum force, expressed as a percentage of the 신율계 게이지 길이, Le (3.5)
3.6.6 percentage total extension at fracture At
total extension (elastic extension plus plastic extension) at the moment of fracture, expressed as a percentage
of the 신율계 게이지 길이, Le (3.5)
자세한 내용, 저희에게 연락하십시오.
지나 승리 악기 (주), 주식 회사
직업적인 시험 장비 제조자
더하다: 아니요. 2-9 킬리허 로드, 리청 지구, 제 남, 산동, 중국.
포스트 코드: 250100
전화: +86-531-68656375
팩스: +86-531-68656375
웹: www.victorytest.com
전자 메일: sales@victorytest.com
증권 시세 표시기- 승리 테스트