ИСО 6892 Metallic materials — Tensile testing —Часть 1:Метод испытаний при комнатной температуре
1 Размах
This part of ISO 6892 specifies the method for tensile testing of metallic materials and defines the mechanical
properties which can be determined at room temperature.
ПРИМЕЧАНИЕ В приложении А указаны дополнительные рекомендации для испытательных машин с компьютерным управлением.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, Применяется только указанное издание. Для недатированных ссылок, the latest edition of the referenced
document (including any amendments) applies.
ИСО 377, Steel and steel products — Location and preparation of samples and test pieces for mechanical
testing
ИСО 2566-1, Steel — Conversion of elongation values — Part 1: Carbon and low alloy steels
ИСО 2566-2, Steel — Conversion of elongation values — Part 2: Austenitic steels
ИСО 7500-1, Metallic materials — Verification of static uniaxial testing machines — Part 1:
Tension/compression testing machines — Verification and calibration of the force-measuring system
ИСО 9513, Metallic materials — Calibration of extensometers used in uniaxial testing
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1 Расчетная длина L
length of the parallel portion of the test piece on which elongation is measured at any moment during the test
3.1.1 original gauge length Lo
length between Расчетная длина (3.1) marks on the piece measured at room temperature before the test
3.1.2 final gauge length after rupture Lu
length between Расчетная длина (3.1) marks on the test piece measured after rupture, at room temperature, the
two pieces having been carefully fitted back together so that their axes lie in a straight line
NOTE Adapted from ISO/TR 25679:2005[3].
3.2 parallel length Lc
length of the parallel reduced section of the test piece.
3.3 elongation
increase in the original gauge length (3.1.1) at any moment during the test
3.4 percentage elongation
elongation expressed as a percentage of the original gauge length, Lo (3.1.1)
3.4.1 percentage permanent elongation
increase in the original gauge length (3.1.1) of a test piece after removal of a specified stress, expressed as a percentage of the original gauge length, Lo
3.4.2 Процентное удлинение после разрушения A
permanent elongation of the gauge length after fracture, (Lu − Lo), expressed as a percentage of the original
Расчетная длина, Lo 1) 5,65 So=5 (4So/ð) .
3.5 длина экстензометра Le
initial extensometer gauge length used for measurement of extension by means of an extensometer
расширение
increase in the длина экстензометра, Le (3.5), at any moment during the test
3.6.1 percentage extension
“strain”
extension expressed as a percentage of the длина экстензометра, Le (3.5)
3.6.2 percentage permanent extension
increase in the extensometer gauge length, after removal of a specified stress from the test piece, expressed
as a percentage of the длина экстензометра, Le (3.5)
3.6.3 percentage yield point extension
See Figure 7.
3.6.4 percentage total extension at maximum force Agt
total extension (elastic extension plus plastic extension) at maximum force, expressed as a percentage of the
длина экстензометра, Le (3.5)
3.6.5 percentage plastic extension at maximum force Ag
plastic extension at maximum force, expressed as a percentage of the длина экстензометра, Le (3.5)
3.6.6 percentage total extension at fracture At
total extension (elastic extension plus plastic extension) at the moment of fracture, expressed as a percentage
of the длина экстензометра, Le (3.5)
Подробнее, пожалуйста, свяжитесь с нами.
ЦЗИНАНЬ ВИКТОРИ ИНСТРУМЕНТ КО., ООО
Производитель профессионального испытательного оборудования
Добавлять: Нет. 2-9 Килихэ Роуд, Район Личэн, Цзинань, Шаньдун, Китай.
Почтовый индекс: 250100
Тель: +86-531-68656375
Факс: +86-531-68656375
Паутина: www.victorytest.com
Электронная почта: sales@victorytest.com
СДС- Испытание на победу